Effect of superficial treatment on the tensile bond strength of two reliners and a thermopolymerizable resin

Authors

  • Cristiane Maria Brasil Leal Professor at the State University of Amazonas
  • Carlos Alberto Muzilli São Leopoldo Mandic
  • Milton Edson Miranda São Leopoldo Mandic
  • José Renato Ribeiro Pinto Pontifícia Universidade Católica de Campinas
  • José Antônio Nunes Mello University of Amazonas

DOI:

https://doi.org/10.20396/bjos.v6i20.8642968

Keywords:

Complete denture. Denture reliners. Dental materials

Abstract

The study aims to evaluate the tensile bond strength of two direct hard reliners, Kooliner and Tokuyama Rebase II and a thermopolymerizable acrylic resin, Vipi Cril, following mechanical superficial treatment. Forty specimens were prepared and separated in four groups according to the relining material and the surface treatment of the thermopolymerizable resin: group I - Kooliner joined to the surface of the resin without treatment, group II - Kooliner joined to the surface of the resin with treatment, group III - Tokuyama joined to the surface of the resin without treatment and group IV - Tokuyama joined to the surface of the resin with treatment. Obtained values were statistically compared by the Bartlett’s test and variance analysis to 5%. The results are presented in Kgf: Group 1, 74.35 ± 15.89; Group 2, 104.95 ± 13.97; Group 3, 86.91 ± 14.63; Group 4, 100.42 ± 14.93. No significant difference was found between the reliners. The mechanical superficial treatment on the thermopolymerizable resin for denture base has significantly increased its tensile bond strength with the studied reliners.

Downloads

Download data is not yet available.

Metrics

Metrics Loading ...

Author Biographies

Cristiane Maria Brasil Leal, Professor at the State University of Amazonas

Possui graduação em Odontologia pela Universidade Federal do Ceará (1987), mestrado em Prótese Dentária pelo Centro de Pesquisas Odontológicas São Leopoldo Mandic (2006) e doutorado em Clínica Odontológica, área de concentração Prótese Dental pela Faculdade de Odontologica de Piracicaba (FOP/UNICAMP). Atualmente é professora da Universidade do Estado do Amazonas. Tem experiência na área de Odontologia, com ênfase em Prótese Dentária, atuando principalmente nos seguintes temas: prótese fixa, estágio I, oclusão e prótese total.

Milton Edson Miranda, São Leopoldo Mandic

- Graduado pela Universidade Federal de Minas Gerais (UFMG);

- Especialização em Prótese pela Associação dos Cirurgiões Dentistas (ACDC);

- Mestrado em Prótese e Oclusão pela Ohio State Univeristy (Columbus,OH ,USA);

- Doutorado pela Universidade de São Paulo(USP).

 

José Renato Ribeiro Pinto, Pontifícia Universidade Católica de Campinas

Possui graduação em Odontologia pela Universidade de São Paulo(1995), especialização em Odontologia pela Universidade de São Paulo(1999), mestrado em Clínica Odontológica pela Universidade Estadual de Campinas(2001), doutorado em Clínica Odontológica pela Universidade Estadual de Campinas(2002), aperfeicoamento em Odontologia pela Universidade de São Paulo(1995), aperfeicoamento em Habilitação em LASERTERAPIA na Odontologia pelo Instituto e Centro de Pesquisas São Leopoldo Mandic(2014), aperfeicoamento em Odontologia pela Universidade de São Paulo(1995) e aperfeicoamento em Odontologia pela Universidade de São Paulo(1994). 

José Antônio Nunes Mello, University of Amazonas

Possui graduação em Odontologia pela Universidade Federal do Amazonas (1993), especialização em Metodologia do Ensino Superior pela Universidade Federal do Amazonas (1996), mestrado em Clínica Odontológica pela Universidade Estadual de Campinas, área de concentração em Prótese Dental (1999) e doutorado em Clínica Odontológica pela Universidade Estadual de Campinas, área de concentração em Prótese Dental (2001). Atualmente é cirurgião-dentista - Secretaria Municipal de Saúde e Professor Adjunto da Universidade do Estado do Amazonas. Tem experiência na área de Odontologia, com ênfase em Materiais Odontológicos, atuando principalmente nos seguintes temas: resina acrílica, microondas, monômero residual, prótese dental e pressão.

References

Leles CR, Machado AL, Vergani CE, Giampaolo ET, Pavarina AC. Bonding strength between a hard chairside reline and a denture base material as influenced by surface treatment. J Oral Rehabil. 2001; 28: 1153-7.

Arena CA, Evans DB, Hilton TJ. A comparison of bond strengths among chairside hard reline materials. J Prosthet Dent. 1993; 70: 126-31.

Arima T, Murata H, Hamada T. Properties of highly crosslinker autopolymerizing reline acrylic resins. J Prosthet Dent. 1995; 73: 55-9.

Cucci ALM, Vergani CE, Giampaolo ET, Pavarina AC, Bercial ME. Resinas para reembasamento imediato: resistência a tração e alongamento. Rev Odontol UNESP. 1998; 27: 299-309.

Murphy WM, Huggett R, Handley RW, Brooks SC. Rigid cold curing resins for direct use in the oral cavity. Br Dent J. 1986; 160: 391-4.

Sekine H, Kishi M, Matsuo E. Development of the noirritation relining material. Bull Tokyo Dent Coll. 1990; 31: 59-61.

Kawano F, Dootz ER, Koran A 3RD, Craig RG. Comparison of bond strength of six denture liners to denture base resin. J Prosthet Dent. 1992; 68: 368-71.

Pinto JRR, Mesquita MF, Henriques GEP, Nóbilo MAA. Effect of thermocycling on bond strength and elasticity of 4 longterm soft denture liners. J Prosthet Dent. 2002; 88: 516-21.

Henriques FQ, Zanetti AL, Elias CN, Feltrin PP, Barbosa MLR. O efeito da termociclagem na resistência adesiva entre materiais rebasers resilientes de silicone com resina acrílica termopolimerizável. PCL Rev Ibero Am Protese Clin Lab. 2006; 8: 43-52.

Bunch J, Johnson GH, Brudvik JS. Evaluation of hard direct reline resins. J Prosthet Dent. 1987; 57: 512-9.

Cucci ALM, Vergani CE, Giampaolo ET, Afonso MCSF. Water sorption, solubility and bond strength of two autopolymerizing acrylic resins and one heat-polymerizing acrylic resin. J Prosthet Dent. 1998; 80: 434-8.

Aydin AK, Terzioglu H, Akinay AE, Ulubayram K, Hasirci N. Bond strength and failure analysis of lining materials to denture resin. Dent Mater. 1999; 15: 211-8.

Arima T, Nikawa H, Hamada T. Composition and effect of denture base resin surface primers for reline acrylic resins. J Prosthet Dent. 1996; 75: 457-62.

Brevilieri EA, Gordilho AC, Raposo CAM, Sanches MJ, Sanches ML. Reembasamento direto de prótese total com resina rígida. Rev Assoc Paul Cir Dent. 2004; 58: 370-3.

Ohkubo C, Takayama Y, Ohkubo E, Nakamura A, Kawai Y, Murakami H et al.[Basic studies on hard direct reline resins. Part 1. adhesive strength]. Tsurumi Shigaku. 1989; 15: 131-8.

Moradians S, Fletcher AM, Amin WM, Richie GM, Purnaveja J, Dodd AW. Some mechanical properties including the repair strength of two self-curing acrylic resins. J Dent. 1982; 10: 271-80.

Shen C, Colaizzi FA, Birns B. Strength of denture repairs as influenced by surface treatment. J Prosthet Dent. 1984; 52: 844-8.

Downloads

Published

2016-01-20

How to Cite

1.
Leal CMB, Muzilli CA, Miranda ME, Pinto JRR, Mello JAN. Effect of superficial treatment on the tensile bond strength of two reliners and a thermopolymerizable resin. Braz. J. Oral Sci. [Internet]. 2016 Jan. 20 [cited 2023 Feb. 8];6(20):1295-300. Available from: https://periodicos.sbu.unicamp.br/ojs/index.php/bjos/article/view/8642968

Issue

Section

Article

Most read articles by the same author(s)