Abstract
Aims: To verify the efficacy of Er,Cr:YSGG laser for debonding of lithium disilicate (LD) reinforced glass ceramic veneers of different thicknesses. Methods: Forty bovine teeth were prepared and randomly divided into four groups (n=10/group) according to the ceramic disc thickness: C0.5 (Control group) and L0.5 (Laser irradiated group) in which LD discs had a thickness of 0.5mm and 5mm diameter; C1 and L1 in which LD discs had a thickness of 1mm and 5mm diameter. The lithium disilcate discs (IPS E.max®, shade HTA2) were fabricated following the manufacturer’s recommendations and cemented to the prepared tooth surface. The Er,Cr:YSGG laser was applied to the laser groups at 2.5W and 25Hz for 60seconds. Universal testing machine was used to evaluate the shear bond strength for all samples at a cross head speed of 1mm/min in an inciso-gingival direction parallel to the sample surface. After debonding, the samples were examined under stereoscope to evaluate the mode of failure according to the adhesive remnant index (ARI). Results: Laser irradiation significantly diminishes the shear bond strength from 10.868 MPa to 3.778 MPa for C0.5 and L0.5 groups respectively (p=0.00) and from 14.711 MPa to 4.992 MPa for C1 and L1 groups respectively (p=0.00). The shear bond strength required for debonding increased with increasing thickness of discs, but without significant difference (p=0.110). Higher ARI scores were seen in the laser groups (more cement remaining adhered to the tooth) when compared to the control groups. Conclusions: The Er,Cr:YSGG laser could be an effective and useful tool in debonding of lithium disilicate ceramic veneers as it decreases the shear bond strength required for veneer debonding.
References
Yilmaz BD, Polat ZS, Izgi AD, Gunduz DT, Dirihan RS. The contribution of ceramic thickness and adhesive type on the de-bonding strength of dental ceramic veneers using Er,Cr:YSGG laser. J Oral Res. 2019 April;8(2):131-9. doi: 10.17126/joralres.2019.021.
Zhang Y, Rocca JP, Fornaini C, Zhen Y, Zhao Z, Merigo E. Erbium-Doped, Yttrium-Aluminum-Garnet Laser Debonding of Porcelain Laminate Veneers: An Ex vivo Study. Contemp Clin Dent. 2018 Oct-Dec;9(4):570-3. doi: 10.4103/ccd.ccd_632_18.
Loffredo MC, Hanashiro FS, Steagall Júnior W, Youssef MN, de Souza-Zaroni WC. Influence of irradiation with Er:YAG laser on the shear bond strength of a resin cement to feldspathic ceramic - in vitro study. Cerâmica. 2015 Apr-Jun;61(358):244-50. doi: 10.1590/0366-69132015613581882.
Azzat A. A novel approach to veneer removal:a clinical case report using Er,Cr:YSGG Laser. Oral Health. 2018 Sep;42-5.
Bajunaid SO. Review of techniques for the intact removal of a permanently cemented restoration. Gen Dent. 2017 Sep-Oct;65(5):48-53.
Oztoprak MO, Tozlu M, Iseri U, Ulkur F, Arun T. Effects of different application durations of scanning laser method on debonding strength of laminate veneers. Lasers Med Sci. 2012 Jul;27(4):713-6. doi: 10.1007/s10103-011-0959-1.
Alikhasi M, Monzavi A, Ebrahimi H, Pirmoradian M, Shamshiri A, Ghazanfari R. Debonding Time and Dental Pulp Temperature With the Er, Cr: YSGG Laser for Debonding Feldespathic and Lithium Disilicate Veneers. J Lasers Med Sci. 2019 Summer;10(3):211-4. doi: 10.15171/jlms.2019.34.
Naseri N, Ghasemi N, Baherimoghadam T, Azmi A. Efficacy of Er,Cr:YSGG laser for debonding of ceramic brackets and prevention of enamel damage and intrapulpal temperature change. Laser Dent Sci. 2020 Aug;4(3):157-63. doi: 10.1007/s41547-020-00101-y.
Oztoprak MO, Nalbantgil D, Erdem S, Tozlu M, Arun T. Debonding of ceramic brackets by a new scanning laser method. Am J Orthod Dentofacial Orthop. 2010 Aug;138(2):195-200. doi: 10.1016/j.ajodo.2009.06.024.
Hayakawa K. Nd:YAG laser for debonding ceramic orthodontic brackets. Am J Orthod Dentofacial Orthop. 2005 Nov;128(5):638-47. doi: 10.1016/j.ajodo.2005.03.018.
Tehranchi A, Fekrazad R, Zafar M, Eslami B, Kalhori KAM, Gutknecht N. Evaluation of the effects of CO2 laser on debonding of orthodontics porcelain brackets vs. the conventional method .Lasers Med Sci. 2011 Sep;26(5):563-67. doi:10.1007/s10103-010-0820-y
Giraldo-Cifuentes H, España-Tost A, Arnabat-Dominguez J. Er,Cr:YSGG laser in the debonding of feldspathic porcelain veneers: an in vitro study of two different fluences. Photobiomod Photomed Laser Surg. 2020 Oct;38(10):640-45. doi: 10.1089/photob.2019.4752
Al-maajoun MK, Henar TE, Tost AE, Terren CA. CO2 and Er,Cr:YSGG Laser applications in debonding ceramic materials: an in vitro study. Open J Dent Oral Med. 2017 Jul;5(3):25-30. doi: 10.13189/ojdom.2017.050301.
.Calabro DE, Puglisi R, Mesquita AMM. Removal of 11 Laminate Veneers with Er-Yag Laser. J Dent Sci. 2019;7(1):63-9.
Karagoz-Yildirak M, Gozneli R. Evaluation of rebonding strengths of leucite and lithium disilicate veneers debonded with an Er:YAG laser. Lasers Med Sci. 2020 Jun;35(4):853-60. doi: 10.1007/s10103-019-02872-8.
Phillips WB. Thermal changes in the dental pulp during Er,Cr:YSGG laser removal of IPS e.max Press Lithium Disilicate Veneers [dissertation]. Ohio State University; 2012 [cited 2021 nov 4]. Available form: http://rave.ohiolink.edu/etdc/view?acc_num=osu1337742959.
Pineda-Vásquez L, Fons-Font A, Bustos-Salvador J, Alonso-Pérez-Barquero J, Román-Rodríguez J. Shear bond strength of debonded ceramic restorations re-cemented by means of a cleaning and retreatment protocol. J Clin Exp Dent. 2019 Jun;11(6):e506-11. doi: 10.4317/jced.55706.
Artun J, Bergland S. Clinical trials with crystal growth conditioning as an alternative to acid-etch enamel pretreatment. Am J Orthod. 1984 Apr;85(4):333-40. doi: 10.1016/0002-9416(84)90190-8.
Yassen GH, Platt JA, Hara AT. Bovine teeth as substitute for human teeth in dental research: a review of literature. J Oral Sci. 2011;53(3):273-82. doi: 10.2334/josnusd.53.273.
Mehl A, Kremers L, Salzmann K, Hickel R. 3D volume-ablation rate and thermal side effects with the Er:YAG and Nd:YAG laser. Dent Mater. 1997 Jul;13(4):246-51. doi: 10.1016/S0109-5641(97)80036-X.
Morshedi E, Zavaree MA, Hakimaneh SMR, Shayegh SS, Pirmoradian M, Torabi S, et al. Effect of Er:YAG laser irradiation on shear bond strength of two porcelain laminate veneers bonded to tooth surface. J Islam Dent Assoc Iran. 2020 Jan;32(1-2):21-9. doi: 10.30699/jidai.32.1.2.21.
Boddun M, Sharva V. Laser hazards and safety in dental practice: a review. Oral Health Care. 2020 Jan;5:1-4. doi: 10.15761/OHC.1000189.
Pradeep S, Anitha SR, Ravi S, Shivalinga BM, Jyothikiran H. Dental lasers: A review of safety essentials. Int J Orthod Rehabil. 2016;7(3):112-4. doi: 10.4103/2349-5243.192535.
Tocchio RM, Williams PT, Mayer FJ, Standing KG. Laser debonding of ceramic orthodontic brackets. Am. J. Orthod Dentofacial Orthop. 1993 Feb;103(2):155-62. doi: 10.1016/ s0889-5406(05)81765-2.
Iseri U, Oztoprak MO, Ozkurt Z, Kazazoglu E, Arun T. Effect of Er:YAG laser on debonding strength of laminate veneers. Eur J Dent . 2014 Jan-Mar;8(1):58-62. doi: 10.4103/1305-7456.126243.
Hussein GAE, Youssef AE, Gutknecht N, Samhan TM. Debonding Of Lithium Disilicate and Feldspathic Veneers with Er, Cr: YSGG Laser Bonded with two different curing mode Resin Cement. AJDS. 2021 Jan;24(1):19-26. doi: 10.21608/ajdsm.2020.48964.1134.
Giraldo-Cifuentes H, Gómez JC, Guerrero ANL Muñoz J. Effect of an Er,Cr:YSGG laser on the debonding of lithium disilicate veneers with four different thicknesses. J Lasers Med Sci. 2020 Fall;11(4):464-8. doi: 10.34172/jlms.2020.72.
Sari T, Tuncel I, Usumez A, Gutknecht N. Transmission of Er:YAG laser through different dental ceramics. Photomed. Laser Surg. 2014 Jan;32(1):37-41. doi: 10.1089/pho.2013.3611.
Tozlu M , Oztoprak MO, Arun T. Comparison of shear bond strengths of ceramic brackets after different time lags between lasing and debonding. Lasers Med Sci. 2012 Nov;27(6):1151-5. doi: 10.1007/s10103-011-1018-7.
This work is licensed under a Creative Commons Attribution 4.0 International License.
Copyright (c) 2021 Sarah Ihsan Al-Araji, Abduladheem Raouf Sulaiman
Downloads